All green sulfolane

May 20, 2023

Scientific Reports volume 13, Article number: 9335 (2023) Cite this article

98 Accesses

3 Altmetric

Metrics details

Industrial commercialization of perovskite solar cells not only depends on sufficient device performance, but also requires complete elimination of hazardous solvents in the fabrication process to enable sustainable development of the technology. This work reports a new solvent system based on sulfolane, \(\gamma\)-butyrolactone (GBL), and acetic acid (AcOH) as a significantly greener alternative to common but more hazardous solvents. Interestingly, this solvent system not only resulted in densely-packed perovskite layer of bigger crystal size and better crystallinity, the grain boundaries were found to be more rigid and highly conductive to electrical current. The physical changes at the grain boundaries were due to the sulfolane-infused crystal interfaces, which were expected to facilitate better charge transfer and provide stronger barrier to moisture within the perovskite layer, yielding higher current density and longer performance of the device as a result. In fact, by using a mixed solvent system consisting of sulfolane, GBL, and AcOH in the volume ratio of 70.0:27.5:2.5, the device stability was better and the photovoltaic performance was statistically comparable with those prepared using DMSO-based solvent. Our report reflects unprecedented findings of enhanced electrical conductivity and rigidity of the perovskite layer simply by using an appropriate choice of the all-green solvent.

The inorganic-organic hybrid perovskite solar cell (PSC) has intrigued many researchers mostly due to its performance potential and promising outlook1,2,3. The rapid development of PSC in recent years also makes it possible to achieve even better photovoltaic performance, especially given the fact that many reported power conversion efficiency (PCE) values have consistently trailed behind the theoretical value of 25.2%3, leaving ample rooms for further achievement. A typical hybrid perovskite crystal structure can be characterized as \(ABX_{3}\), which consists of cation (A site), such as CH\(_{3}\)NH\(_{3}^{+}\), HC(NH\(_{2}\))\(_{2}^{+}\), Cs\(^{+}\), and Rb\(^{+}\). The inorganic framework \(BX_{3}\) consists of halide elements (X site) and the metal (B site), such as Pb\(^{+}\) and Sn\(^{+}\)4. The recently reported PCE has reached up to 25.2%3, a level that represents a significant advance especially when compared with other photovoltaics, such as CdTe, copper indium gallium selenide (CIGS), as well as dye-sensitized and organic solar cells5.

Equally important to the development of photovoltaic performance is the impact on the environment and human health of the preparation process. Reports of high performance often relied on the use of hazardous chemicals, such as carcinogenic N-methyl-2-pyrrolidone (NMP) and N,N-dimethylformamide (DMF) and highly skin-penetrating dimethyl sulfoxide (DMSO), for the preparation of perovskite6,7,8,9,10. However, even though the use of these solvents could warrant high device performance, their toxicity toward the environment and human health could cause serious issues, especially when the technology is implemented at large scale10. Therefore, to develop PSC technology in a sustainable manner, the issue over the choice of solvents needs to be addressed.

In an effort toward greener preparation, the mixed solvent consisting of polyethylene glycol and \(\gamma\)-butyrolactone (GBL) was used to prepare the PbBr\(_{2}\) precursor solution. The resulting PSC showed a PCE of up to 8.11%11. (R)-(+)-Limonene and 2-methyltetrahydrofuran could also be used as less-toxic antisolvents in the preparation of high-quality perovskite layer in the inverted PSC device, with PCE of up to 17.84%12. Tian and coworkers also suggested n-butanol as a green antisolvent for preparing perovskite films in large-area devices, which demonstrated a PCE of 13.85%13. Yavari and coworkers used anisole as a green antisolvent in the preparation of PSCs, which yielded impressive PCE of up to 20.5%14. Nevertheless, despite many efforts so far, the device stability remains a challenge14, which could be attributed to inefficient dissolution of perovskite precursors in the preparation process15. As a result, complete elimination of hazadous solvents has yet to materialize, and these solvents still play a role to varying degree in the fabrication process to facilitate solubility of chemical precursors.

In this work, the issue of solubility of perovskite precursors, particularly PbI\(_{2}\) for methylammonium lead(II) iodide perovskite, was tackled in order to determine alternative solvent system for the preparation of perovskite. Based on the Hansen solubility analysis in assessing the solubility of PbI\(_{2}\)15, sulfolane (1\(\lambda ^{6}\)-thiolane-1,1-dione or tetramethylene sulfone) emerged as a promising solvent that contains a sulfone functional group similar to DMSO16. In addition to very low skin penetration in comparison with other solvents16, sulfolane is a polar aprotic solvent with high miscibility, which makes it possible to be used in mixed solvents with various other compounds. The relatively high viscosity and boiling point of sulfolane would not only help reduce vapor pressure within the devices during normal operation, but also promote better occupational health and safety for future large-scale manufacturing. To formulate green solvent alternative based on sulfolane17, green additive such as acetic acid (AcOH) was also introduced to assist the solubility of PbI\(_{2}\) by reducing the supersaturated concentration of the precursor and facilitating the formation of pre-nucleation cluster18. In addition, green component such as \(\gamma\)-butyrolactone (GBL) was also used in the solvent mix to improve the solubility of PbI\(_{2}\) in accordance with the Hansen solubility concept10,19,20.

The results showed that a new mixed solvent system consisting of sulfolane, GBL, and AcOH could deliver a PCE that was statistically comparable to the control device fabricated using toxic DMSO-based solvent. Perhaps more importantly, the 10-days stability test under 48–50% relative humidity revealed that the device fabricated using the sulfolane-based solvent became more stable. Surprisingly, the results showed that a new mixed solvent system consisting of sulfolane, GBL, and AcOH could enhance electrical conductivity and rigidity of the perovskite layer, which in turn delivered cell performance that was statistically comparable to the control device fabricated using toxic DMSO-based solvent. The stability test under 48–50% relative humidity also revealed that the device fabricated using the sulfolane-based solvent was more stable at least for over 10 days of testing.

Transparent, conductive, fluorine-doped tin oxide (FTO) glass (surface resistivity: 7 \(\Omega\)/sq) substrates were purchased from Solaronix. For the synthesis of TiO\(_{2}\) compact layer, titanium isopropoxide (TTIP) and titanium(IV) butoxide (Ti(OBu)\(_{4}\)) from Fluka Analytical were used. Ethanol (95%) from Sigma-Aldrich was used as the solvent for the synthesis. Titanium chloride (TiCl\(_{4}\)) was used for the surface treatment of the TiO\(_{2}\) layer. For the perovskite solution, PbI\(_{2}\) (99.99%), CH\(_{3}\)NH\(_{3}\)I (99.5%), 2,2\(^\prime\),7,7\(^\prime\)-tetrakis (N, N-di-p-methoxyphenilamine)-9,9\(^\prime\)-spirobiflourene (spiro-OMeTAD, 99.5%), lithium bis-(trifluoromethanesulfonyl) imide (Li-TFSI, 99.9%), and 4-tert-butylpyridine (TBP, 96%) were purchased from Sigma-Aldrich. Titanium(IV) isopropoxide (99.999%), chlorobenzene (99.9%), N,N-dimethylformamide (DMF, 99.9%), dimethyl sulfoxide (DMSO, anhydrous 99.9%), \(\gamma\)-butyrolactone (GBL), sulfolane, acetic acid (AcOH, 99%), and acetonitrile (99.9%) were also obtained from Sigma Aldrich. For the metal evaporation, gold metal (99.99%) and silver metal (99.9%) were purchased from Kurt J. Lesker company.

The sol–gel method was used to prepare the TiO\(_{2}\) compact layer. First, TTIP was mixed with ethanol (95%) using the volume ratio 7.83:92.17. Then 60 \(\upmu\)L of concentrated HCl was slowly added into the solution. The solution was stirred overnight before being coated on an FTO glass using spin coating method. Finally, TiCl\(_{4}\) solution was used to treat the surface of the TiO\(_{2}\) layer.

The fluorine-doped tin oxide (FTO) glass was cleaned in 3 sequential steps (Alconox detergent, water, and isopropanol) and then dried using N\(_{2}\) gas. The process of each step was conducted under high relative humidity of 48–52%. TTIP was coated onto the FTO glass as an electron transport layer (ETL) using spin coating at 2000 rpm for 30 s, which was followed by annealing at 550 \(^\circ\)C for 1 h and a cool-down to room temperature. TiCl\(_{4}\) solution was used to treat the TiO\(_{2}\) surface and air-dried on a hotplate at 500 \(^\circ\)C for 2 h. After the substrate cool down, a solution containing 1.5 mol L\(^{-1}\) PbI\(_{2}\) and 1.5 mol L\(^{-1}\) CH\(_{3}\)NH\(_{3}\)I (or MAI) was coated on a substrate using two-step spin coating method at 1500 rpm for 7 s and then at 3500 rpm for 50 s, followed by annealing at 80 \(^\circ\)C for 20 min. The solvents used in this step were GBL:DMSO of volume ratio 70:30 (denoted as GBL:DMSO), GBL:sulfolane of volume ratio 70:30 (denoted as GBL:sulfolane), and GBL:sulfolane:AcOH of volume ratio 70:27.5:2.5 (denoted as GBL:sulfolane:AcOH), which had been optimized according to the Hansen solubility model as shown in Table S1. The optimized volume ratio of GBL (70):DMSO (30) reported in the previous work20 was used as the control sample. The spiro-OMeTAD was prepared by dissolving 72.3 mg of spiro-OMeTAD, 28.8 \(\upmu\)L of TBP, and 17.5 \(\upmu\)L of Li-TFSI solution (520 mg of Li-TFSI in 1 mL of acetonitrile) in 1 mL chlorobenzene. The solution was then spin-coated onto the perovskite layer using two sequential steps (at 1500 and 4000 rpm) for 50 s each to obtain a hole transport layer (HTL). In a final step, gold metal was deposited via thermal evaporation as a counter electrode. The device structure can be denoted as FTO/c-TiO\(_{2}\)/MAPbI\(_{3}\)/HTL/Au.

The current density–voltage (J–V) parameters of the measured devices were obtained by using an NREL calibrated Keithley Model 2400 under simulated AM 1.5G solar irradiation at 100 mW cm\(^{-2}\). The forward scan was operated from − 0.1 to 1.1 V. The ultraviolet–visible spectroscopy (UV–Vis) spectra were measured using a UV–Vis spectrophotometer (Shimadzu UV-2600). The photoluminescence (PL) was performed by using Horiba Fluro Max 4, with excitation at 500 nm and emission from 600 to 900 nm. The device structure used for the PL measurement was FTO/perovskite. Atomic force microscopy (AFM) measurements were carried out by using Park NX-10 with Forta cantilever with 1.6 N m\(^{-1}\) spring constant. The AFM setup was calibrated using a sapphire sample. The topography images were obtained at a speed of 10 \(\upmu\)m s\(^{-1}\), and the force slopes were collected with 0.2 N m\(^{-1}\) set point. Surface current mapping for J\(_{sc}\) and V\(_{oc}\) conditions were done by conductive contact mode with a platinum iridium5 (PtIr\(_{5}\))-coated PPP-CONTSCPt cantilever that has a 0.2 N m\(^{-1}\) spring constant and resonance frequency of 25 kHz. The scan speed was 2 \(\upmu\)m\(^{-1}\) and the setpoint at 15 nN under 0.2 mW cm\(^{-2}\) illumination of microscope light with the bias − 0.6 V for V\(_{oc}\) current mapping and without bias for J\(_{sc}\) current mapping. The X-ray diffraction (XRD) measurement was performed using a PANalytical Aris with a setting at 8 mA and 40 kV. The XPS results were obtained using a Thermo Scientific (UK) with an X-ray source of monochromated Al 150 W.

SEM and topological AFM images of \(5.0 \times 5.0 \upmu\)m in area of the perovskite films fabricated using (a and b) GBL:DMSO, (c and d) GBL:sulfolane, and (e and f) GBL:sulfolane:AcOH, respectively.

The top-view scanning electron microscopy (SEM) images of perovskite films fabricated using different solvents are shown in Fig. 1a,c,e. The results illustrated that, for perovskite film prepared using mixed solvent of GBL:sulfolane:AcOH, the crystals formed were more densely packed compared to the control sample prepared using GBL:DMSO. The perovskite crystals for the case of GBL:DMSO showed smaller sizes and higher amount of grain boundaries (Fig. 1a). This is in stark contrast to the formation of perovskite crystals using GBL:sulfolane and GBL:sulfolane:AcOH that showed larger crystal sizes of perovskite (Fig. 1c,e) resulting in increased surface roughness. The AFM topography images were consistent with the SEM images shown in Fig. 1b,d,f.

XRD patterns of the perovskite films prepared using different solvent systems. The zoom-in shows the peaks about 31.84\(^\circ\), which corresponds to MAPbI\(_{3}\)-sulfolane phase21.

The quality of perovskite crystals was assessed by using XRD measurement on FTO/c-TiO\(_{2}\)/MAPbI\(_{3}\). According to Fig. 2, the patterns of perovskite CH\(_{3}\)NH\(_{3}\)PbI\(_{3}\) (or MAPbI\(_{3}\)) at 14.02\(^\circ\), 28.4\(^\circ\), and 31.84\(^\circ\) can be indexed as (110), (220), and (310), respectively22,23,24,25. The XRD patterns, especially at the peak position of 31.84\(^\circ\)24, showed that the perovskite film prepared using a new solvent system of either GBL:sulfolane or GBL:sulfolane:AcOH revealed higher crystallinity when compared with the control sample prepared using GBL:DMSO. The improved crystallinity as a result of the sulfolane-based solvents, could be associated with the formation of the MAPbI\(_{3}\)-sulfolane close interaction21, while the structure of perovskite remained unchanged26,27. Furthermore, the crystal size calculated using the Scherrer's equation for perovskite material prepared using GBL:sulfolane and GBL:sulfolane:AcOH was larger than those prepared using GBL:DMSO (see Table 1 and Fig. 1). The perovskite film prepared using GBL:sulfolane:AcOH showed no evidence of PbI\(_{2}\) at 12.7\(^\circ\), which indicated complete conversion of PbI\(_{2}\) to perovskite28,29,30.

FTIR spectra of perovskite film prepared using different solvent systems.

It is interesting to note that the sulfolane-based solvents used in the perovskite preparation could play a role in the formation of perovskite layer. In fact, the FTIR peak positions of 440 and 1147 cm\(^{-1}\) for the perovskite layer prepared using GBL:sulfolane and GBL:sulfolane:AcOH (Fig. 3) correspond to characteristic bonding of sulfolane in the perovskite films31,32 which also affirms the presence of MAPbI\(_{3}\)-sulfolane. The formation of MAPbI\(_{3}\)-sulfolane was further revealed by the XPS results. While most peaks of Pb\(_{4f7/2}\), Pb\(_{4f5/2}\)33, I\(_{3d}\) (Fig. 4a,b), as well as other peaks (Supplementary Fig. S1) were essentially similar among the perovskite prepared using different solvents, a significant red shift in C\(_{1s}\) occurred with the case of GBL:sulfolane and GBL:sulfolane:AcOH (Fig. 4c). The lower binding energy observed for the case of sulfolane-based solvents could indicate strong solvation of the methylammonium cations (CH\(_{3}\)NH\(_{3}^{+}\)or MA\(^{+}\)) in perovskite by oxygen atoms in sulfonyl group16. Particularly in case of GBl:sulfolane:AcoH, interaction between MA\(^{+}\) in perovskite and the carbonyl group of AcOH was possible34, resulting in chemical passivation33,34. Together with the XRD and IR spectra (Figs. 2 and 3), the presence of strong interaction between MAPbI\(_{3}\) and sulfolane likely helped decelerate the crystallization process of perovskite33, which resulted in bigger perovskite crystals21.

XPS results of perovskite prepared using different solvent systems.

In order to assess whether the presence of sulfolane and/or AcOH in the perovskite layer could translate into physical properties of the perovskite layer, mechanical pinpoint AFM was used to study the surface topography and mechanical properties of the layer. As revealed in Supplementary Fig. S2d–f, on average, the perovskite prepared using GBL:sulfolane and GBL:sulfolane:AcOH showed higher modulus than that of the perovskite film prepared using GBL:DMSO. Similarly, the deformation of perovskite films prepared using sulfolane-based solvents was lower than that of the sample prepared in DMSO-based solvent (Supplementary Fig. S3d–f). The increased rigidity of the perovskite layer when prepared using sulfolane-based solvents could be attributed to the presence of sulfolane, possibly in the areas of grain boundaries. Such an increased in rigidity may also help impede the penetration of moisture into the grain boundaries of the perovskite film, which could lead to better stability of the device35. These results were also consistent with the adhesion mapping shown in Supplementary Fig. S3a–c35,36.

c-AFM (3D) and top surface current mapping (2D) at 0 V and at bias − 0.6 V (V\(_{oc}\) mapping) of the perovskite films fabricated using (a–c) GBL:DMSO, (d–f) GBL:sulfolane, and (g-i) GBL:sulfolane:AcOH, respectively.

To probe the electronic properties of the surface of perovskite, conductive atomic force microscopy (c-AFM) was performed to obtain current mapping with no external bias under the illumination of microscope light with power 0.2 mW cm\(^{-2}\). According to the results shown in Fig. 5d,e,g,h, the perovskite layers prepared using GBL:sulfolane and GBL:sulfolane:AcOH revealed average current of 75 pA and 96 pA, respectively, which were significantly higher than 33 pA of the sample prepared using GBL:DMSO (Fig. 5a,b). The improved charge transfer on the conductive surface when sulfolane-based solvents were used to fabricate the perovskite layer was likely originated from the presence of electron-rich, high-dipole moment sulfolane molecules37,38, at the grain boundaries of the perovskite39. This is consistent with the surface electrical current profiles shown in Supplementary Fig. S4d–f. The higher current density indicated enhancement in conductivity, especially with the solvent GBL:sulfolane:AcOH (Fig. 5g,h), which could facilitate better carrier separation and improve the short-circuit current density (J\(_{sc}\)) of the device33.

To further investigate electrical properties of the perovskite layer, V\(_{oc}\) mapping (current maps under reverse bias) was measured in which a reverse bias of − 0.6 V was used to block the current generated at the normal band from hole blocking ability of electron transport layer and observe the current at the position of lower V\(_{oc}\) area with high density of trap sites. The perovskite layers prepared using GBL:sulfolane and GBL:sulfolane:AcOH showed higher current leakage (Fig. 5f,i) when compared with the perovskite prepared using GBL:DMSO (Fig. 5c). The degree of current leakage indicates the degree of trap recombination sites at the surface of perovskite40. It is interesting to also note that, although the grain boundaries of perovskite prepared with sulfolane-based solvents showed favorable electrical current as revealed by c-AFM, the presence of trap recombination was rather significant and still posed an issue for device performance.

Light properties of perovskite films prepared using different solvent systems.

As shown in the UV–Vis spectra in Fig. 6a, minor differences in absorption intensity were observed at visible wavelengths among the perovskite samples prepared using different solvent systems. The onset of perovskite absorption remained essentially the same at 765 nm for all solvent conditions. However, the steady-state photoluminescence (PL) revealed significant differences when different solvents were used for the preparation of the device structure FTO/MAPbI\(_{3}\). According to Fig. 6b, using GBL:sulfolane or GBL:sulfolane:AcOH showed higher PL intensity when compared to the case of GBL:DMSO. This result suggests that the perovskite prepared using sulfolane-based solvents likely showed higher radiative emission11,41, which is consistent with the cAFM results (Fig. 5g–i,), as well as higher current density (Table 2). We noted that all perovskite layers prepared using different solvent systems did not significantly differ in terms of thickness (see Supplementary Fig. S5).

To assess the relative influence between the electron-hole and trap recombination, the time-resolved photoluminescence (TRPL) was also performed and analyzed via bi-exponential fit42.

According to Supplementary Table S2 and Fig. S6, the perovskite prepared using sulfolane-based solvents showed higher fraction of short-time component (\(\alpha\)2), which can be attributed to trap recombination at the perovskite interfaces41-consistent with the V\(_{oc}\) mapping in Fig. 5c,f,i. Although the sulfolane-based solvent resulted in more trap sites, the average carrier lifetime was not significantly different from that of the perovskite prepared with GBL:DMSO (Supplementary Table S2). This could be due to the large crystal size of perovskite, especially in the presence of acetic acid in the solvent system, which prolonged the electron-hole recombination time component and helped recover V\(_{oc}\) loss due to trap sites33.

Device performance for perovskite prepared using different solvent systems.

According to the analysis of the J–V results (See Supplementary Fig. S7), the efficiency of the devices fabricated using GBL:sulfolane:AcOH was \(13.60\pm 1.45\)%, which was statistically similar to the value of \(14.90 \pm 1.94\)% for the control devices prepared using GBL:DMSO. As reported in Table 2 and shown in Fig. 7a,b, J\(_{sc}\) of the devices fabricated using GBL:sulfolane:AcOH was higher in value compared with the control one prepared using GBL:DMSO. The enhanced J\(_{sc}\) was likely due to higher crystallinity and conductivity of perovskite crystals, as suggested in Figs. 2 and 6b. Although the use of sulfolane-based solvents inadvertently increased the trap sites that affected V\(_{oc}\), the chemical passivation of acetic acid in GBL:sulfolane:AcOH helped recover the V\(_{oc}\) loss33. As a result, the V\(_{oc}\) of device prepared with GBL:sulfolane:AcOH was essentially unchanged compared to the case of DMSO based solvent (Table 2). The fill factor (FF) of the devices fabricated using sulfolane-based solvents was, however, lower than the case of DMSO-based solvent (Fig. 7c). This could be attributed to the surface roughness of perovskite crystals prepared using sulfolane-based solvents (see Fig. 1), possibly preventing close interfaces between perovskite and adjacent layers22.

Average device performance during a period of 10 days under 48–52% RH for encapsulated PSC devices prepared using different solvent systems.

The use of sulfolane-based solvents not only yielded the performance on par with DMSO-based solvent, but also resulted in greater device stability over at least 10 days of testing. According to Fig. 8, the PSC devices prepared using GBL:sulfolane and GBL:sulfolane:AcOH revealed good stability. The unencapsulated devices prepared using GBL:sulfolane and GBL:sulfolane:AcOH showed about 5% drop in PCE under relative humidity (RH) of 48–50% (Fig. 8a). J\(_{sc}\) and V\(_{oc}\) also showed favorable trend for sulfolane-based solvents, revealing drops of about 8 mA cm\(^{-2}\) and 0.01 V in J\(_{sc}\) and V\(_{oc}\), respectively (Fig. 8b,c). On the contrary, the control sample prepared using GBL:DMSO showed rapid deterioration in PCE, J\(_{sc}\), and V\(_{oc}\) by 9%, 10 mA cm\(^{-2}\), and 0.02 V, respectively. Such a rapid decrease in performance was likely due to the smaller grain size with no passivation of sulfolane in perovskite15,22. Overall, these results indicated that the use of eco-friendly sulfolane-based solvents could improve both the device efficiency and the long-term performance. The use of acetic acid in the solvents led to more uniform crystals of perovskite and also helped eliminating unreacted PbI\(_{2}\) that would have resulted in lower stability and efficiency of the devices15,31.

The optimal condition for the all green solvent based on nontoxic sulfolane, GBL, and AcOH for the preparation of perovskite was reported. The perovskite crystals prepared using GBL:sulfolane and GBL:sulfolane:AcOH showed larger crystal sizes with higher rigidity. In contrast, the perovskite crystals prepared using GBL:DMSO were loosely packed with more grain boundaries. The XRD pattern also confirmed high crystallinity and preferential orientation of perovskite crystals when prepared using the green solvents reported. The steady-state PL also revealed higher radiative emission when sulfolane-based solvents were used in the preparation. With the presence of sulfolane remaining at the grain boundaries, the cAFM results indicated a significantly improved electrical conductivity was improved. Even though sulfolane-infused grain boundaries inadvertently promoted trap sites, strong interaction between perovskite and sulfolane, as well as acetic acid passivation, helped counter any loss in performance. In terms of the photovoltaic performance, PCE of \(13.6 \pm 1.45\)%, which was statistically comparable to \(14.9 \pm 1.94\)% of the control sample, was observed when the sulfolane-based solvents were used. Such a satisfactory conversion efficiency can be attributed to relatively high J\(_{sc}\), afforded by improved crystallinity and conductive surface of perovskite.

When observed over a period of 10 days under high relative humidity of 48–52% without device encapsulation, the PSC devices prepared using GBL:sulfolane and GBL:sulfolane:AcOH showed stability superior to the case of DMSO-based solvent. Thus, the sulfolane-based solvents not only could yield better overall performance of the devices, but also offer environmentally conscientious approach toward present and future development of PSC. As large-scale PSC production becomes progressively feasible, these green alternative solvents could play an increasingly important role in protecting human health and minimizing detrimental impact on the environment.

The datasets used and/or analyzed during the current study are available from the corresponding author on reasonable request.

Tong, X., Lin, F., Wu, J. & Wang, Z. M. High performance perovskite solar cells. Adv. Sci. 3(5), 1500201 (2016).

Article Google Scholar

Shih, Y.-C. et al. Amino-acid-induced preferential orientation of perovskite crystals for enhancing interfacial charge transfer and photovoltaic performance. Small 13(22), 1604305 (2017).

Article Google Scholar

Dai, T. et al. Strategies for high-performance large-area perovskite solar cells toward commercialization. Crystals 11(3), 295 (2021).

Article CAS Google Scholar

Whalley, L. D., Frost, J. M., Jung, Y. K. & Walsh, A. Perspective: Theory and simulation of hybrid halide perovskites. J. Chem. Phys. 146, 220901 (2017).

Article ADS PubMed PubMed Central Google Scholar

Green, M. et al. Solar cell efficiency tables (version 57). Prog. Photovolt. Res. Appl. 29(1), 3–15 (2021).

Article Google Scholar

Saidaminov, M. I. et al. High-quality bulk hybrid perovskite single crystals within minutes by inverse temperature crystallization. Nat. Commun. 6, 7586 (2015).

Article ADS PubMed Google Scholar

Pham, N. D. et al. Enhanced perovskite electronic properties via a modified lead(ii) chloride lewis acid-base adduct and their effect in high-efficiency perovskite solar cells. J. Mater. Chem. 5, 5195–5203 (2017).

Article CAS Google Scholar

Donald, J. M., Hooper, K. & Hopenhayn-Rich, C. Reproductive and developmental toxicity of toluene: A review. Environ. Health Perspect. 94, 237–244 (1991).

CAS PubMed PubMed Central Google Scholar

Lee, K., Chromey, N., Culik, R., Barnes, J. & Schneider, P. Toxicity of n-methyl-2-pyrrolidone (nmp): Teratogenic, subchronic, and two-year inhalation studies. Fundam. Appl. Toxicol. 9(2), 222–235 (1987).

Article CAS PubMed Google Scholar

Gardner, K. L. et al. Nonhazardous solvent systems for processing perovskite photovoltaics. Adv. Energy Mater. 6(14), 1600386 (2016).

Article Google Scholar

Cao, X. et al. All green solvents for fabrication of CsPbBr\(_{3}\) films for efficient solar cells guided by the hansen solubility theory. Solar RRL 4(6), 2000209 (2020).

Article CAS Google Scholar

Sang, H. P., In, S. J. & Jae, W. J. Green solvent engineering for environment-friendly fabrication of high-performance perovskite solar cells. Chem. Eng. J. 425, 131475 (2021).

Article Google Scholar

Tian, S. et al. A facile green solvent engineering for up-scaling perovskite solar cell modules. Sol. Energy 183, 386–391 (2019).

Article ADS CAS Google Scholar

Yavari, M. et al. Greener, nonhalogenated solvent systems for highly efficient perovskite solar cells. Adv. Energy Mater. 8(21), 1800177 (2018).

Article ADS Google Scholar

Krishnan, U., Kaur, M., Kumar, M. & Kumar, A. Factors affecting the stability of perovskite solar cells: A comprehensive review. J. Photon. Energy 9(2), 021001 (2019).

ADS CAS Google Scholar

Tilstam, U. Sulfolane: A versatile dipolar aprotic solvent. Org. Process Res. Dev. 16(7), 1273–1278 (2012).

Article CAS Google Scholar

Katon, J. & Feairheller, W. The vibrational spectra and molecular configuration of sulfolane. Spectrochim. Acta 21(1), 199–201 (1965).

Article ADS CAS Google Scholar

Su, Y. et al. Acetic acid-assisted synergistic modulation of crystallization kinetics and inhibition of Sn\(_{2}^{+}\) oxidation in tin-based perovskite solar cells. Adv. Func. Mater. 32(12), 2109631 (2022).

Article CAS Google Scholar

Babaei, A. et al. Hansen theory applied to the identification of nonhazardous solvents for hybrid perovskite thin-films processing. Polyhedron 147, 9–14 (2018).

Article CAS Google Scholar

Siripraparat, A., Ponchai, J., Kanjanaboos, P. & Pakawatpanurut, P. Efficiency enhancement of perovskite solar cells by using ag- or ag-cu composite-doped surface passivation of the electron transport layer. Appl. Surf. Sci. 562, 150147 (2021).

Article CAS Google Scholar

Jiang, X. et al. One-step synthesis of SnI\(_{2} \cdot\)(DMSO)x adducts for high-performance tin perovskite solar cells. J. Am. Chem. Soc. 143(29), 10970–10976 (2021).

Article CAS PubMed Google Scholar

Wen, Y., Tang, Y.-G. & Yan, G.-Q. Large grain size CH\(_{3}\)NH\(_{3}\)PbI\(_{3}\) film for perovskite solar cells with hydroic acid additive. AIP Adv. 8(9), 095226 (2018).

Article ADS Google Scholar

Jeon, N. J. et al. Solvent engineering for high-performance inorganic-organic hybrid perovskite solar cells. Nat. Mater. 13, 897–903 (2014).

Article ADS CAS PubMed Google Scholar

Ahn, N. et al. Highly reproducible perovskite solar cells with average efficiency of 18.3% and best efficiency of 19.7% fabricated via lewis base adduct of lead(ii) iodide. J. Am. Chem. Soc. 137(27), 8696–8699 (2015).

Article CAS PubMed Google Scholar

Moore, D. T. et al. Crystallization kinetics of organic-inorganic trihalide perovskites and the role of the lead anion in crystal growth. J. Am. Chem. Soc. 137(6), 2350–2358 (2015).

Article CAS PubMed Google Scholar

Zheng, G. et al. Manipulation of facet orientation in hybrid perovskite polycrystalline films by cation cascade. Nat. Commun. 9, 2793 (2018).

Article ADS PubMed PubMed Central Google Scholar

Aboud, A. A., Shaban, M. & Revaprasadu, N. Effect of Cu, Ni and Pb doping on the photo-electrochemical activity of ZnO thin films. RSC Adv. 9, 7729–7736 (2019).

Article ADS CAS PubMed PubMed Central Google Scholar

Hu, S. et al. Light-induced photoluminescence quenching and degradation in quasi 2D perovskites film of (C\(_{6}\)H\(_{5}\)C\(_{2}\)H\(_{4}\)NH\(_{3}\))\(_{2}\) (CH\(_{3}\)NH\(_{3}\))\(_{2}\)[Pb\(_{3}\)I\(_{10}\)]. Appl. Sci. 11(6), 2683 (2021).

Article CAS Google Scholar

Wu, Y. et al. Perovskite solar cells with 18.21% efficiency and area over 1 cm\(^2\) fabricated by heterojunction engineering. Nat. Energy 1, 16148 (2016).

Article ADS CAS Google Scholar

Kim, H.-S. et al. High efficiency solid-state sensitized solar cell-based on submicrometer rutile TiO\(_2\) nanorod and CH\(_{3}\)NH\(_{3}\)PbI\(_{3}\) perovskite sensitizer. Nano Lett. 13(6), 2412–2417 (2013).

Article ADS CAS PubMed Google Scholar

Zhang, W. et al. Solvent-induced textured structure and improved crystallinity for high performance perovskite solar cells. Opt. Mater. Express 7, 2150–2160 (2017).

Article ADS CAS Google Scholar

Walter, T., Herberholz, R., Müller, C. & Schock, H. W. Determination of defect distributions from admittance measurements and application to Cu(In, Ga)Se\(_{2}\) based heterojunctions. J. Appl. Phys. 80(8), 4411–4420 (1996).

Article ADS CAS Google Scholar

Li, Y. et al. Acetic acid assisted crystallization strategy for high efficiency and long-term stable perovskite solar cell. Adv. Sci. 7(5), 1903368 (2020).

Article CAS Google Scholar

Peng, J. et al. A universal double-side passivation for high open-circuit voltage in perovskite solar cells: Role of carbonyl groups in poly(methyl methacrylate). Adv. Energy Mater. 8(30), 1801208 (2018).

Article Google Scholar

Fairfield, D. J. et al. Structure and chemical stability in perovskite-polymer hybrid photovoltaic materials. J. Mater. Chem. A 7, 1687–1699 (2019).

Article CAS Google Scholar

Kim, W. et al. Enhanced long-term stability of perovskite solar cells by passivating grain boundary with polydimethylsiloxane (pdms). J. Mater. Chem. A 7, 20832–20839 (2019).

Article CAS Google Scholar

Qin, T.-X. et al. Quantification of electron accumulation at grain boundaries in perovskite polycrystalline films by correlative infrared-spectroscopic nanoimaging and kelvin probe force microscopy. Light Sci. Appl. 10, 84 (2021).

Article ADS PubMed PubMed Central Google Scholar

Derr, J. B., Tamayo, J., Espinoza, E. M., Clark, J. A. & Vullev, V. I. Dipole-induced effects on charge transfer and charge transport: Why do molecular electrets matter? Can. J. Chem. 96(9), 843–858 (2018).

Article CAS Google Scholar

Marszalek, M. et al. Ionic liquid-sulfolane composite electrolytes for high-performance and stable dye-sensitized solar cells. Adv. Energy Mater. 4(6), 1301235 (2014).

Article Google Scholar

Via, F. . La. . et al. New approaches and understandings in the growth of cubic silicon carbide. Materials 14(18), 5348 (2021).

Article ADS CAS PubMed PubMed Central Google Scholar

Teng, P. et al. Elegant face-down liquid-space-restricted deposition of CsPbBr\(_{3}\) films for efficient carbon-based all-inorganic planar perovskite solar cells. ACS Appl. Mater. Interfaces 10(11), 9541–9546 (2018).

Article CAS PubMed Google Scholar

Sillen, A. & Engelborghs, Y. The correct use of "average’’ fluorescence parameters. Photochem. Photobiol. 67(5), 475–486 (1998).

CAS Google Scholar

Download references

This work was supported by the Science Achievement Scholarship of Thailand (SAST), Mahidol University (Basic Research Fund: fiscal year 2021), the NSRF via the Program Management Unit for Human Resources & Institutional Development, Research and Innovation (grant number B16F640099), and the Center of Excellence for Innovation in Chemistry (PERCH-CIC), Ministry of Higher Education, Science, Research and Innovation, Thailand.

These authors contributed equally: Akarapitch Siripraparat and Pimolrat Mittanonsakul.

Department of Chemistry, Faculty of Science, Mahidol University, Bangkok, 10400, Thailand

Akarapitch Siripraparat, Pimolrat Mittanonsakul & Pasit Pakawatpanurut

Center of Excellence for Innovation in Chemistry (PERCH-CIC), Faculty of Science, Mahidol University, Bangkok, 10400, Thailand

Akarapitch Siripraparat, Pongsakorn Kanjanaboos & Pasit Pakawatpanurut

School of Materials Science and Innovation, Faculty of Science, Mahidol University, Bangkok, 10400, Thailand

Pimsuda Pansa-Ngat, Chaowaphat Seriwattanachai & Pongsakorn Kanjanaboos

National Nanotechnology Center (NANOTEC), National Science and Technology Development Agency, Thailand Science Park, Khlong Luang District, Pathum Thani, 12120, Thailand

Pisist Kumnorkaew & Anusit Kaewprajak

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

A.S.: Writing—original draft, methodology, validation, data curation. P.M.: Writing—editing, conceptualization, investigation. P.P.: Writing—editing, methodology, data curation. C.S.: Writing—editing, methodology, data curation. P.K.: Methodology, investigation. A.K.: Methodology, investigation. P.K.: writing—editing, methodology, data curation. P.P.: Writing—editing, conceptualization, methodology, data curation.

Correspondence to Pasit Pakawatpanurut.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Siripraparat, A., Mittanonsakul, P., Pansa-Ngat, P. et al. All green sulfolane-based solvent enhanced electrical conductivity and rigidity of perovskite crystalline layer. Sci Rep 13, 9335 (2023). https://doi.org/10.1038/s41598-023-36440-6

Download citation

Received: 10 January 2023

Accepted: 03 June 2023

Published: 08 June 2023

DOI: https://doi.org/10.1038/s41598-023-36440-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.